Slickote M1 Air Dry Solid Film Lubricant Mil-PRF-46147C Ty1 & 2 /Lead Free /Low VOC Product Description Slickote M1 is an air cured, low voc resin bonded solid film
lubricant coating which meets the requirements of Mil-PRF-46147C Ty 1 and 2. Intended Use To
reduce wear and prevent galling, corrosion and seizure of metals. Where conventional lubricants are difficult to apply or retain, or where
other lubricants may be easily For sliding motion applications such as plain and spherical bearings, flap tracks, hinges, threads and cam surfaces. Where
temperature ranges are from -67 deg
C to 93 deg C (-88 deg F to 200 deg F) When
mechanisms are operated at infrequent intervals or are lubricated for life. Where
long term corrosion protection is required under static conditions. Where extremely heavy loaded lubrication is required including initial start up of heavy loaded mechanisms designed for fluid lubrication. As a
touch up to worn surfaces previously coated with solid film lubrication Application Procedure Metal Preparation: All surfaces must be thoroughly cleaned, degreased,
free of rust, oxides or other surface Aluminum – Anodize and seal iaw Mil-A-8625, type II, Class 1
(non-dyed). Steel – Abrasive clean (180 to 220 grit aluminum oxide) and
phosphate coat iaw DOD-P-16232 type M or Z,
Class 3. Stainless Steel - Abrasive clean (120 grit aluminum oxide)
and Passivate iaw AMS QQ-P-35. Titanium – Abrasive Clean
(180 to 220 grit aluminum oxide) and alkaline anodize. 1)
Mix well, in mechanical paint shaker 2)
Concentrate only: Reduce with SlicKote Reducer 1:1 (or 50/50 mix of Acetone
& Oxsol 100 by Wt) 3) Apply with spray gun, brushing or dipping:
to .008 mm to .013 mm coating
thickness (.0002 to .0005 inch) 4)
Air dry for 30 minutes Physical Properties Color:
#1 Grey (natural), #2
Grey/Black Dilution:
Concentrate: Reduce with SlicKote Reducer 2:1 by
volume (or 50% Acetone/ Oxsol100) Wt/Gal
9.96 Lbs/gal App.temp:
Ambient (< 90 degF)
Cure:
Air Dry 18 Hours
Shelf Life: 1 year from date of manufacture Storage:
Store in closed container VOC:
<135 g/l Solids:
Concentrate:
25% Viscosity:
Zahn #1, 30 sec Do
not use in food processing or handling equipment or surfaces with food contact.
Use only in well ventilated area or hood where no flames or other ignition
sources are present. Product Description Solvent base, air dried resin bonded coating based on
Mil-PRF-46147C Uses exempt solvents to achieve low voc, <135 g/l
(meets both type 1 and 2 requirements) Lead and Graphite Free Used to provide a thin coating with exceptional
protection aganist wear and corrosion. Operating temp range: -88 deg F to +200 deg F Coating Thickness:
.0002 to .0005 inch Properties:
Tested in accordance with Mil-PRF-46147 Film Adhesion
ASTM D-2510A
Pass Thermal Stability
ASTM D-2511
Pass Salt Spray
ASTM B-117, >100 Hr
Pass Fluid Resistance
*Mil-PRF-7808, Aircraft Turbine Oil
Pass
*SAE J1966 gd50, Aircraft Oil
Pass
*Mil-PRF-372, Cleaning Cmpd
Pass
*ASTM D-1193, Reagent Water
Pass
*Mil-H-46170, Hydraulic Fluid
Pass
*Mil-DTL-83133, JP-8
Pass
*Mil-L-PRF-32033, Lube Oil
Pass
*VV-D-1078, Silicone Fluid
Pass
*Mil-L-14107, Weapon Lube Oil
Pass
*Mil-L-46000, Semi Fluid Lubricant
Pass
*Mil-L-63460, Cleaner & Preserve
Pass Wear Properties
ASTM D-2625A, Endurance Life >120 min
ASTM D-2625B, Load Capacity >250 Lbf
|